JOINT 3173007 - Caterpillar

Illustration 2 g03863748
Inside of crack in Illustration 1
Illustration 3 g03863751
Small crack at weld start
Illustration 4 g03863758
Weld crack in Illustration 3 extending into the base edge
Illustration 5 g03863752
Typical base edge failure from type of crack in Illustrations 1 and 2.
Illustration 6 g03863755
Typical base edge failure from type of crack in Illustrations 3 and 4.Loader and excavator base edge components are composed of hardened steel to resist high load stresses and abrasion. Components operating in a long wear life situation may eventually fail from fatigue, as will those components subjected to severe stresses. Most base edge failures begin as small cracks at the adapter weld starts. Some cracks may occur shortly after build completion due to improper weld application.Any small crack, as shown in Illustrations 1 through 4, when detected but considered as being inconsequential and requiring no immediate repair, can eventually develop into a major failure as shown in Illustrations 5 and 6.Often there is a tendency to repair these small cracks by just welding over the crack. However, the original welds must be gouged out completely before making a repair. Any part of the crack remaining under a "repaired weld" will propagate further along the adapter weld or deeper into the base edge until there is a complete failure similar to those failures shown in Illustrations 5 and 6.
Illustration 7 g03863759
Illustration 8 g03863760
Base edges and adapters have a high enough Carbon Equivalent to require preheating to 150° - 220° C (300° - 428° F). Before gouging out the crack to full depth, preheat the area on either side of the crack equal to three times the thickness of the base edge Illustration 7. Remove the heating source and wait at least one minute before checking for a temperature drop. Reheat the area if the temperature drops more than 10° C (50° F). Thin base edges, 25.4 mm (1.0 inch) or under, can easily overheat during welding and only minimal preheating is normally required.Preheating adapters above 220° C (428° F) can cause loss of toughness, hardness, strength, and wear resistance. An interpass temperature up to 260° C (500° F) is acceptable as this temperature is only a temporary condition that could be reached between weld passes. Check the preheat temperature with temperature sticks/crayons or an infrared thermometer as shown in Illustration 8. Infrared thermometers are subject to emissivity differences of various surface conditions. Infrared thermometers should be checked first against temperature sticks or crayons to verify what the corrected reading should be.
Illustration 9 g03863763
Gouged out crack
Illustration 10 g03863764
Replaced adapter weld after edge repair
Illustration 11 g03863766
Slag removal after each weld passIf the crack propagates as the carbon arc gouging approaches the end of the crack, lance or drill the ends of the crack before continuing on. Since most base edge failures begin at the start of the adapter weld, a portion of that weld should also be removed (Illustration 9). Check for any crack remaining with dye check. Remove the dye penetrant before making a weld repair. Then use E71T-1 low hydrogen wire or E7018 stick electrode to fill in