SUPPORT GP-SEAT 2358856 - Caterpillar

Field Follow Observations
During the field follow of machines, nitrite depletion from 500 parts per million (ppm) to 0 ppm was observed. Simultaneously, the pH level of the coolant increased, and the odor of ammonia appeared. Continued operation of the field follow machines at 0 ppm nitrite showed a disappearance of the ammonia smell and the pH level returned to normal levels. The cooling systems continued to function normally throughout the field follow period.In some cases, Cat ELC Extender was added to boost the nitrite level back to 500 ppm. The situation reoccurred until the nitrite was again depleted back to 0 ppm. Having a high pH and an ammonia smell in the coolant is not desired.Recommended Actions
For machines without wet sleeve liners (engines smaller than C8.8), the secondary cavitation protection that nitrite provides is not needed. Therefore, on machines with aluminum radiators and without wet sleeve liners, when nitrite is depleted and pH levels are elevated, it is recommended to dose the cooling system with the appropriate amount of Cat 369-0805 Additive (Cooling Conditioner for Aluminum Components). Do not add any Cat ELC Extender until mid-life of the coolant, and continue to operate the machines with depleted nitrite.
For machines with wet sleeve liners (engines larger than C8.8), secondary corrosion erosion protection from nitrite is still needed. Therefore, on machines with aluminum radiators and wet sleeve liners, when nitrite is depleted and pH is elevated, dose the cooling system with the appropriate amount of Cat 369-0805 Additive (Cooling Conditioner for Aluminum Components). Also, add an amount of Cat ELC Extender equal to 1% total cooling system capacity to boost the nitrite concentration to within an acceptable range for proper corrosion erosion protection.Cat S∙O∙S Level 2 coolant analysis is recommended within 500 hours after either of the actions listed above. Be sure to note on the sample label if Cat 369-0805 Additive (Cooling Conditioner for Aluminum Components) and/or Cat ELC Extender was added prior to taking the follow-up Level 2 coolant sample.Note: This article only addresses ELC and not conventional coolants, as in Diesel Engine Antifreeze/Coolant (DEAC). In the case of DEAC and other conventional type coolants, nitrite provides almost all the cavitation erosion corrosion protection. It is necessary to maintain appropriate nitrite levels in these coolants.